[关键词]
[摘要]
目的 分析桃胶改良前后的多糖含量、影响制剂的功能性质以及体外释放度变化情况,探索其变化规律,为改良桃胶作为新型缓释辅料的应用提供依据。方法 将不同产地原桃胶与改良桃胶烘干、粉碎、过筛,粉末用超纯水超声溶解,采用苯酚-硫酸法结合紫外-可见分光光度法测定多糖质量分数;pH计测定胶液的酸碱度;Brookfield DV-II Pro黏度计测定胶液的动力黏度;称重法测定胶粉溶解度及溶胀度;干燥器控制法测定胶粉不同相对湿度环境下的吸湿率;体外释放度实验结合HPLC法测定喘平方胶片中3个指标成分(麻黄碱、伪麻黄碱和东莨菪碱)的体外累积释放度。结果 贵州习水、江西信丰、湖北随县产原桃胶各指标为多糖质量分数为84.30%、81.52%、77.84%;1%胶溶液pH值为5.63、5.60、5.88;1%胶溶液动力黏度为30.8、28.5、25.9 mPa·s;水中溶解度为60.8、57.5、51.2 mg/g;溶胀度为34.22%、29.66%、26.25%;12 h的相对湿度(RH)43%吸湿率为28.19%、27.02%、26.44%,RH 81%吸湿率为38.22%、35.26%、34.64%;喘平方胶片中麻黄碱、伪麻黄碱和东莨菪碱2 h的体外累积释放度为95.41%~98.84%、96.05%~97.11%、96.35%~98.21%。贵州习水、江西信丰、湖北随县产改良桃胶,各指标为多糖质量分数为96.92%、94.76%、93.65%;1%胶溶液pH值为7.07、7.08、7.12;1%胶溶液动力黏度为318.4、289.6、266.4 mPa·s;水中溶解度为178.2、167.3、163.8 mg/g;溶胀度为84.98%、81.55%、79.82%;12 h的RH 43%吸湿率为41.22%、39.93%、39.20%,RH 81%吸湿率为60.88%、58.48%、57.17%;喘平方胶片中麻黄碱、伪麻黄碱和东莨菪碱12 h的体外累积释放度为97.88%~98.36%、97.59%~98.56%、97.72%~98.12%。结论 与原桃胶相比,改良桃胶在多糖含量、溶解度、溶胀度、动力黏度、吸湿率、缓释性能等方面均显著提高,且溶液呈现中性,提示可作为新型缓释材料进一步研发、应用。
[Key word]
[Abstract]
Objective To analyze the difference of polysaccharides content, property characterization, and in vitro release between the original peach gum and improved peach gum, and to find the change rule, so as to provide the basis for its further application as the new delivery material. Methods The content of polysaccharides was measured by the phenol-sulfuric acid method combined with ultraviolet spectrophotometry. The pH value of liquid cement was measured by pH meter. The dynamic viscosity of liquid cement was measured by the Brookfield DV-Ⅱ Pro viscometer. The solubility and swelling ratio of rubber powder were measured by the weighing method. The moisture-absorption rate at different relative humidity of rubber powder was measured by the method of controlling humidity with the desiccator. With three index components (ephedrine, pseudoephedrine, and scopolamine) as the standards, HPLC and the release test were applied to determine the accumulated release rate of Chuanping adhesive tablets (CAT). Results Original peach gum:In the three producing areas of Xishui in Guizhou Province, Xinfeng in Jiangxi Province, and Suixian in Hubei Province, the content of polysaccharides respectively was 84.30%, 81.52%, and 77.84%. The pH value of 1% liquid cement was 5.63, 5.60, and 5.88. The dynamic viscosity of 1% liquid cement was 30.8, 28.5, and 25.9 mPa·s. The solubility of rubber powder was 6.08%, 5.75%, and 5.12%. The swelling ratio of rubber powder was 34.22%, 29.66%, and 26.25%. The 12 h moisture-absorption rate of the improved peach gum polysaccharose at RH of 43% was 28.19%, 27.02%, and 26.44%; and at RH of 81% was 38.22%, 35.26%, and 34.64%. The 2 h cumulative release amount in vitro of methamphetamine, pseudoephedrine, and scopolamine of Chuanping adhesive tablets were 95.41%-98.84%, 96.05%-97.11%, and 96.35%-98.21%. Improved peach gum:In the three producing areas of Xishui, Xinfeng, and Suixian, the content of polysaccharides respectively was 96.92%, 94.76%, and 93.35%. The pH of 1% liquid cement was 7.10, 7.08, and 7.12. The dynamic viscosity of 1% liquid cement was 318.4, 289.6, and 266.4 mPa·s. The solubility of rubber powder was 17.82, 16.73, and 16.38 g. The swelling ratio of rubber powder was 84.98%, 81.55%, and 79.82%. The 12 h moisture-absorption rate of the improved peach gum polysaccharose at RH of 43% was 41.22%, 39.93%, and 39.20%; and at RH of 81% was 60.88%, 58.48%, and 57.17%. The 12 h cumulative release amount in vitro of methamphetamine, pseudoephedrine, and scopolamine of CAT were 97.88%-98.36%, 97.59%-98.56%, and 97.72%-98.12%. Conclusion Compared with the original peach each gum, the content of polysaccharides, dynamic viscosity, solubility, swelling ratio, and moisture-absorption rate, and sustained release property of the improved peach gum were all improved remarkably, and the solution was also neutral. These results show that the improved peach gum can be further developed and applied as a new sustained release material.
[中图分类号]
[基金项目]
国家自然科学基金青年基金项目(81503260);国家自然科学基金面上项目(81373981)