目的 研究参芪妇康颗粒干法制粒最佳成型工艺条件。方法 以颗粒的一次性成型率和吸湿率作为评价指标,采用L9(34)正交试验法优选最佳辅料配比。结果 以干浸膏-微粉硅胶-可溶性淀粉-麦芽糊精77.5:2.5:5:15为最佳辅料配比;干法制粒工艺条件参数为车间温度20℃,50%相对湿度,挤压压力12 kg/cm3,侧封压力14 kg/cm3,挤压频率22 Hz,制粒频率52 Hz,送料频率19 Hz。结论 优选的参芪妇康颗粒干法制粒成型工艺稳定可行,成品流动性、溶化性良好,吸湿性小,为大生产提供了可靠实验依据。
[Key word]
[Abstract]
Objective To study the optimum molding process condition of dry granulating of Shenqi Fukang Granules (SFG). Methods Using primary formation rate and hygroscopicity rate as evaluation indicators; The optimal excipient ratio was optimized by L9(34) orthogonal test method. Results The ratio of dry extract-micro silica gel-soluble starch-maltodextrin 77.5:2.5:5:15 was the optimal ratio of excipients; Dry granulating conditions parameters:workshop temperature of 20℃, relative humidity of 50%, extrusion pressure of 12 kg/cm3, side seal pressure of 14 kg/cm3, extrusion frequency of 22 Hz, granulation frequency of 52 Hz, and feeding frequency of 19 Hz. Conclusion The optimized SFG dry granulating molding process is stable and feasible. The finished product showed a fine liquidity, good dissolubility and little hygroscopicity, which provides a reliable experimental basis for large-scale production.
[中图分类号]
[基金项目]
三亚市医疗卫生科技创新项目:参芪妇康颗粒的研制(2016YW03)